Nd,Ce：YAG

YAG is an excellent laser material used for no-water cooling and miniature laser systems

Classification:

Detailed introduction

Nd:Ce:YAG is an excellent laser material used for no-water cooling and miniature laser systems.The thermal distortion of Nd:Ce:YAG is appreciably less and the output laser energy is greater(30%-50%)than that in Nd:YAG at the same pumping.It is the most ideal laser material for air cooling laser and is also suitable for different modes of operation(pulsed,Q-switched,mode locked)and high-average power lasers.

PRODUCT FEATURE

High slope efficiency,Low threshold

High optical quality

Good anti-UV irradiation property

Good thermal stability

Good repetition frequency

Specifications:

Specifications
Concentration	Nd:1.0at%~1.1at%, Ce:0.05at%~0.1atm%
Orientation	<111> or <100>±5°
Dimension	Diameter:1mm~40mm,Length:0.3mm~150mm (Customized available)
Dimension Tolerance	Φ:+0/-0.04mm,L:+0.5/-0mm
Perpendicularity	≤5′
Parallelism	≤10″
Chamfer	0.15±0.05mm
Clear Aperture	>95%
Scratch Quality	10/5(MIL-PRF-13830B)
Barrel finish	Fine Ground, Polishing, Grooving
Flatness	≤λ/10@632.8nm
Wavefront Distortion	≤λ/10 per inch@632.8nm
Extinction Ratio	≥30dB
Coating	AR coating:R<0.15%@1064nm,R<0.5%@808nm,R<0.15%@532nm
	PR coating :R=(10~90)%±2%@1064nm
	HR coating:R>99.8%@1064nm,R>99.8%@808nm
Damage Threshold	≥1GW/cm2@1064nm,10ns,10Hz

Optical properties
Laser Transition	⁴F_3/2→⁴I_11/2
Laser Wavelength	1064nm
Photon Energy	1.86×10^-19J@1064nm
Emission Line-width	4.5Å@1.064μm
Emission Cross Section	2.7~8.8×10^-19cm²@Nd1at%
Fluorescence Lifetime	230μs@Nd1at%
Absorption Wavelength of Diode Pumped	808nm

Physical and Chemical Properties
Crystal Structure	Cubic
Melting Point	1970°
Density	4.56±0.04g/cm³
Specific Heat	0.59J/g.cm³@0~20℃
Elasticity Modulus	310GPa
Young’s Modulus	3.17×10⁴Kg/mm²
Mohs Hardness	8.5
Poisson’s Ratio	0.3
Tensile Strength	0.13~0.26GPa
Thermal Shock Resistance	790W/m
Thermal Expansion Coefficient	<100>orientation:8.2×10^-6/K@0~250°C
	<110>orientation: 7.7×10^-6/K@0~250°C
	<111>orientation:7.8×10^-6/K@0~250°C
Thermal Conductivity	14W/m/K@20℃
Thermal Conductivity	10.5W/m/K@100℃
Thermal Optical Coefficient	7.3×10^-6/K
Refractive Index	1.8197@1064nm
Solubility	Insoluble in water, slightly soluble in ordinary acid